| Recommended printing conditions | Nozzle Temperature250-280℃Recommended Nozzle Diameter0.4-1.0 mmRecommended build surface treatmentGlass、PEI Film or PC FilmBuild plate temperature70-80 °CChamber TempN/ACooling fan speed0-50%Print speed30-300 mm/sRetraction distance1-3 mmRetraction speed1800-2400 mm/minDrying setting60-70℃ for 4-6hAnnealingN/A |
|---|
| | Nozzle Temperature250-280℃Recommended Nozzle Diameter0.4-1.0 mmRecommended build surface treatmentGlass、PEI Film or PC FilmBuild plate temperature70-80 °CChamber TempN/ACooling fan speed0-50%Print speed30-300 mm/sRetraction distance1-3 mmRetraction speed1800-2400 mm/minDrying setting60-70℃ for 4-6hAnnealingN/A |
|---|
Printing Tips：1.The wear resistance of copper nozzle is poor. It is recommended to use stainless steel or hardened steel nozzle to print, which can effectively improve the printing quality.2.Please put filament into a dry box, which can effectively reduce the oozing, rough surface and so on.
暂无匹配的打印配置文件。
以下参数同步自关联的产品参数管理V2，可作为切片与试打调参的起点。
同步自产品参数管理V2的温度、速度与冷却建议。
喷嘴、底板以及打印前准备建议。
支撑材料、支撑间距和兼容耗材建议。
没有匹配的问题，请尝试其他关键词。
通用安全提示（FusRock）
| 短期不使用时 | 放入密封防潮盒或进行简易抽真空即可，避免阳光直射。 |
|---|---|
| 长期不使用 | 将耗材放入出厂铝箔袋并尽量排出袋内空气（条件允许时在袋内再放一包干燥干燥剂）；外套一层家用抽真空保鲜袋后抽真空。置于阴凉干燥处，避免阳光直射。 |
PTC 小型烘干盒：60–70℃，烘干 4–6 小时。
小型恒温鼓风烘干机：箱内温度场往往不均匀，可能导致料盘变形；此类设备上建议适当降低温度并缩短单次烘干时间（示例：40–45℃，约 4 小时），并结合材料详情中的干燥建议综合判断。
重要：若按此温度烘干后打印效果仍无改善，请先用空料盘做温度测试，再酌情提高烘干温度，以防温度过高或不均匀导致料盘烘干变形。
大型恒温鼓风烘干机：60–70℃，烘干 4–6 小时。
PS：为什么不同烘干设备适用温度会有差别？可在后台插入说明或外链「点击了解」。
⚠ 操作前请阅读
（可插入「变形 vs 正常」料盘对比照片，注意控制烘干温度与摆放方式。）
耗材受潮的影响
| 未受潮 | 受潮 |
|---|---|
| 表面相对整洁、颜色正常、力学性能在规格内 | 可能出现痘痕/毛刺/拉丝、颜色发白、力学性能下降等（因材料而异） |
（可插入 RH80% 环境下拆封后第 1 / 2 / 3 天打印同一模型的对比图。）
* 上述吸湿对比示例可能因产品系列而异（例如 PAHT-CF），请在插入图片时于脚注中注明材料系列。