一款高流动性的TPU95A-HF柔性3D打印材料
产品简介
FusFlex™️ TPU95A-HF是一款易打印的TPU材料。在同等硬度下，FusFlexTM TPU95A-HF相比其他常规TPU耗材会更容易被挤出，当选用合适的挤出机时，FusFlexTM TPU95A-HF可支持100mm/s以上的打印速度。
物性表
测试项目 Property | 测试方法 Testing method | 典型值 Typical value |
密度 Density | ISO 1183 | 1.15 g/cm³ |
硬度 Hardness | ISO 7619 | 95A |
熔融指数 Melt index | 200℃，2.16kg | 30 g/10min |
维卡软温度 Vicat softening temperature | ISO 306 | 99°C |
拉伸断裂强度 (X-Y) Tensile breaking strength (X-Y) | ISO 527 | 31.81±3.26 MPa |
断裂伸长率100% (X-Y) elongation at break (X-Y) | 471±81 % | |
100%定伸应力 (X-Y) tensile stress at 100% (X-Y) | 9.75±0.16 MPa | |
200%定伸应力 (X-Y) tensile stress at 200% (X-Y) | 12.2±0.27 MPa | |
300%定伸应力 (X-Y) tensile stress at 300% (X-Y) | 17.0±0.49 MPa |
试样打印参数：喷嘴大小0.4mm，喷嘴温度210°C，底板加热50°C，打印速度60mm/s，填充率100%，填充角度±45°
Specimens printed under the following conditions: Nozzle size 0.4mm，Nozzle temp 210°C, Bed temp 50°C, Print speed 60mm/s, Infill 100%, Infill angle ±45°
建议打印参数
喷头温度 Nozzle temperature | 210-230°C |
建议喷嘴大小 Recommended nozzle diameter | ≥0.2mm |
建议底板材质 Recommended build surface | 玻璃，PEI膜或PC膜 Glass, PEI Film or PC Film |
底板温度 Build plate temperature | 20-50°C |
Raft间距 Raft separation distance | 0.18-0.22mm |
冷却风扇 Cooling fan speed | On |
打印速度 Print speed | 30-120 mm/s |
回抽距离 Retraction distance | 1-5 mm |
回抽速度 Retraction speed | 1800-3600 mm/min |
其他建议： Additional Suggestions： 1. 如果想实现高速打印，推荐使用近程挤出机，例如：BMG挤出机、Titan挤出机、Hemera挤出机，并适当提高喷嘴温度。 If you want to achieve high-speed printing, it is recommended to use direct extruders, such as BMG extruder, Titan extruder and Hemera extruder, and appropriately increase the nozzle temperature.
2. TPU材料暴露在空气中容易吸收水分，吸湿后打印会出现拉丝，挤出有气泡，打印表面粗糙等现象，降低打印质量。建议您打开FusFlexTM TPU95A-HF真空铝箔袋包装后立即将线材放入干燥盒内（湿度控制在15%以下）进行打印。不用的线材请放回原包装铝箔袋内密封保存。 TPU material is very easy to absorb moisture when exposed to air, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the FusFlex™ TPU95A-HF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
3. 材料受潮后会出现打印拉丝增多，挤出有气泡，打印表面质量粗糙等现象。请将线材放入70-80℃烘箱内干燥4-6h，即可恢复FusFlexTM TPU95A-HF的打印质量。 After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 70-80℃ for 4-6h to restore the printing quality of FusFlex™ TPU95A-HF. | |